Buchumschlag

Methods for assessing corrosion hydrogen degradation of oil-gas piplenes steels

Gespeichert in:

Bibliographische Detailangaben
Datum:	2020
Hauptverfasser:	O. I. Zvirko, Ye. I. Kryzhanivskyi, H. M. Nykyforchyn, H. V. Krechkovska
Format:	Artikel
Sprache:	Englisch
Veröffentlicht:	2020
Schriftenreihe:	Materials Science (Physicochemical mechanics of materials)
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0001187400
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

Peculiarities of corrosion-hydrogen degradation of oil and gas pipelines and oil tanks
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2011)

Develop¬ment of in-laboratory method of steel degradation for assessing their crack growth resistance
von: M. I. Hredil, et al.
Veröffentlicht: (2021)

Corrosion degradation of long-term operated gas pipeline elbow with macrodefect
von: O. I. Zvirko, et al.
Veröffentlicht: (2016)

Corrosion and corrosion-mechanical fracture of crude oil tank steel
von: Yu. Petryna, et al.
Veröffentlicht: (2015)

Assessment of the service degradation of a gas pipeline steel by destructive and non-destructive method
von: Yu. V. Milman, et al.
Veröffentlicht: (2011)

Fractographic features of service degradation of welds in main oil pipelines
von: H. V. Krechkovska, et al.
Veröffentlicht: (2015)

Estimation of stresses caused by electrochemical hydrogenation of pipe carbon steel
von: O. I. Zvirko, et al.
Veröffentlicht: (2024)

The influence of the structural-mechanical state of the transit gas pipeline steel on the susceptibility to hydrogen embrittlement
von: O. I. Zvirko, et al.
Veröffentlicht: (2024)

Use of electrochemical methods for evaluation of operational degradation of structural steels
von: O. I. Zvirko
Veröffentlicht: (2016)

Method of laboratory degradation of structural steels
von: O. T. Tsyrulnyk, et al.
Veröffentlicht: (2017)

Biocorrosion and localization of degradation processes on main gas pipeline steel surface
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2019)

The influence of hydrogenation of oil-and-gas pipeline walls on their soil corrosion and life
von: O. V. Hembara, et al.
Veröffentlicht: (2011)

Electrochemical methods of evaluation of degradation of long-term operation structural steels
von: O. I. Zvirko
Veröffentlicht: (2016)

Diagnostic signs of degradation of pressure regulator of the gas transport system
von: H. V. Krechkovska, et al.
Veröffentlicht: (2016)

Assessment of steam pipeline steels degradation by impact toughness on the specimens with a cut of different-geometry
von: H. V. Krechkovska, et al.
Veröffentlicht: (2016)

The evaluation of operational degradation of gas pipeline steels by the mechanical stability criterion
von: Yu. Ya. Mieshkov, et al.
Veröffentlicht: (2014)

Operational degradation of structural steels (A review)
von: O. I. Zvirko
Veröffentlicht: (2021)

Methods of improving corrosion resistance of tubes made of low-alloy steels for the gas-and-oil producing industry
von: T. O. Derhach, et al.
Veröffentlicht: (2020)

Diagnostics of pipe steel susceptibility to property degradation as a result of long-term operation
von: H. M. Nykyforchyn, et al.
Veröffentlicht: (2016)

Safety assessment of the transit oil- and gas-pipelines with corrosion pits
von: Toth, L., et al.
Veröffentlicht: (2009)

Degradation of 09H2S steel in the conditions of oil-refining
von: O. H. Arkhypov, et al.
Veröffentlicht: (2010)

Assessment of residual lifetime of oil pipes with outer surface corrosive mechanical crack under oil laminar flow and reusable hydroblow
von: Ye. Andreikiv, et al.
Veröffentlicht: (2017)

Scientific support for development of oil and gas industry
von: Ye. I. Kryzhanivskyi
Veröffentlicht: (2015)

Fractographic features of hydrogen transport mechanisms in structural steels
von: H. V. Krechkovska
Veröffentlicht: (2015)

The role of non-metal inclusions in premature corrosion- mechanical failure of drill pipes
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2019)

Evaluation of service degradation of profile steel of edge-forming boom
von: Ye. V. Kharchenko, et al.
Veröffentlicht: (2013)

The influence of steels structure on corrosion, hydrogenation, stress corrosion cracking in hydrogen suplhide environments
von: M. S. Khoma, et al.
Veröffentlicht: (2019)

Numerical analysis of the regularities of the infuence of pipe steel degradation on the reliability of corroded main gas pipelines used for transportation of gas-hydrogen mixtures
von: O. S. Milenin, et al.
Veröffentlicht: (2024)

Ranking of mechanical characteristics of HPP pipeline steels by their sensitivity to operational degradation
von: O. Z. Student, et al.
Veröffentlicht: (2021)

Eeletrochemical method of diagnostics of sea portal cranes degradation
von: O. O. Nemchuk, et al.
Veröffentlicht: (2020)

Operation degradation of 20Kh13 steel blades of HPP steam turbines
von: H. M. Nykyforchyn, et al.
Veröffentlicht: (2011)

The effect of hydrogen sulfide on the corrosion and mechanical properties of pipe steel welded joints
von: H. V. Chumalo
Veröffentlicht: (2012)

Degradation of welded joint metal of the exploited main gas pipeline
von: O. T. Tsyrulnyk, et al.
Veröffentlicht: (2010)

Assessment of degradation of the steel of pipelines by their structural, mechanical and electromechanical characteristics
von: O. P. Ostash, et al.
Veröffentlicht: (2010)

Mathematical modeling of hydrogen influence on corrosion activity of steel structures
von: Song Wen-Guang, et al.
Veröffentlicht: (2020)

The influence of hydrogen sulphide concentration on corrosion and hydrogenation of pipe steels (A review)
von: M. S. Khoma, et al.
Veröffentlicht: (2021)

Problems and prospects of transporting a mixture of green hydrogen and natural gas in the context of the development of hydrogen energy in Ukraine
von: O. I. Zvirko
Veröffentlicht: (2024)

Anisotropy of the mechanical properties of 15Kh1M1F degraded steel after its exploitation on HPP pipelines
von: O. Z. Student, et al.
Veröffentlicht: (2011)

Corrosion and hydrogenation of 09H2S steel in hydrogen sulphide environments at elevated temperatures and pressures.
von: M. S. Khoma, et al.
Veröffentlicht: (2015)

Corrosion and hydrogenation of 17H1S-U steel in hydrogen sulfide media of different concentrations
von: V. I. Pokhmurskyi, et al.
Veröffentlicht: (2020)