Procedure of accelerated corrosion testing for modelling the long-term effect of moderate climate atmosphere on welded joints

Procedure of accelerated corrosion testing for modelling the long-term effect of moderate climate atmosphere on welded joints

Gespeichert in:

Bibliographische Detailangaben
Datum:	2019
Hauptverfasser:	V. V. Knysh, S. O. Osadchuk, S. O. Solovei, L. I. Nyrkova, A. O. Rybakov
Format:	Artikel
Sprache:	English
Veröffentlicht:	2019
Schriftenreihe:	Automatic Welding
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0001076348
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

The influence of high-frequency mechanical impact strengthening of the butt welded joints of 15KhSND steel on their atmospheric corrosion and resistance to fatigue fracture
von: V. V. Knysh, et al.
Veröffentlicht: (2018)

Application of high-frequency peening to improve the performance of butt welded joints in the atmosphere of temperate climate
von: V. V. Knysh, et al.
Veröffentlicht: (2017)

Influence of high-frequency peening and atmosphere of marine climate on the cyclic life of T-welded joints with surface fatigue cracks
von: V. V. Knysh, et al.
Veröffentlicht: (2020)

The influence of high-frequency peening on corrosion fatigue of welded joints
von: V. V. Knysh, et al.
Veröffentlicht: (2017)

Investigation of carbon steel atmospheric corrosion under formation of adsorption and phase water layers
von: L. I. Nyrkova, et al.
Veröffentlicht: (2012)

On the determination of atmospheric corrosion rate of metal constructions using polarization resistance method
von: L. I. Nyrkova, et al.
Veröffentlicht: (2011)

The influence of marine environment on fatigue life of butt welded joints of 15KhSND steel, strengthened by high-frequency mechanical impact
von: V. V. Knysh, et al.
Veröffentlicht: (2019)

Methodological approach and criterion of the estimation of pipe steel susceptibility to stress corrosion cracking
von: L. I. Nyrkova, et al.
Veröffentlicht: (2019)

Development of a sensor to determine the rate of corrosion of welded metal structures under atmospheric conditions
von: S. A. Osadchuk, et al.
Veröffentlicht: (2011)

Stress-corrosion cracking of Kh70 pipe steel at a potential approximated to the maximum protection potential
von: L. I. Nyrkova, et al.
Veröffentlicht: (2018)

Creation of energy efficient "green constructions" in conditions of moderately continental climate
von: Tkachenko, T.M.
Veröffentlicht: (2018)

Corrosion and mechanical durability of welded joints of aluminum alloy V1341, produced by argon-arc welding by free and constricted arc
von: L. I. Nyrkova, et al.
Veröffentlicht: (2020)

Corrosion-mechanical resistance of welded joints of AMg5M alloy produced in different spatial positions of butts
von: L. I. Nyrkova, et al.
Veröffentlicht: (2022)

Influence of corrosion damages on cyclic life of butt welded joints strengthened by high-frequency mechanical peening
von: V. V. Knysh, et al.
Veröffentlicht: (2018)

Creation of energy efficient "green constructions" in conditions of moderately continental climate
von: T. M. Tkachenko
Veröffentlicht: (2018)

Analysis of causes of failure of site welded butt joints of main pipelines after long-term operation
von: L. I. Nyrkova, et al.
Veröffentlicht: (2023)

Effect of corrosion damages on cyclic life of welded T-joints treated by high-frequency mechanical peening
von: V. V. Knysh, et al.
Veröffentlicht: (2016)

Investigation of corrosion of enamel cold water supply pipes
von: S. O. Osadchuk, et al.
Veröffentlicht: (2023)

The influence of corrosive environment on the correlation of cathode protection current and limit diffusion current for the X70 pipe steel
von: L. I. Nyrkova, et al.
Veröffentlicht: (2020)

Hydraulic testing of pipe sections with corrosion damage in the mode of low-cycle loading
von: P. S. Jukhimets, et al.
Veröffentlicht: (2013)

Development of ultrasonic testing procedures and determination of performance of the assembly of the joint of header to steam generator PGV-1000M
von: A. V. Dub, et al.
Veröffentlicht: (2014)

Plasma acceleration in the atmosphere by pulsed inductive thruster
von: Korytchenko, K. V., et al.
Veröffentlicht: (2024)

Corrosion degradation of long-term operated gas pipeline elbow with macrodefect
von: O. I. Zvirko, et al.
Veröffentlicht: (2016)

Causes of stress corrosion fracture of site circumferential joint of main gas pipeline
von: A. A. Rybakov, et al.
Veröffentlicht: (2014)

Corrosion-mechanical resistance of 2219 alloy welded joints, under simulated service conitions
von: L. I. Nyrkova, et al.
Veröffentlicht: (2021)

Renewable power in the system of long-term national measures as for adapting to climate changes
von: M. M. Khvorov
Veröffentlicht: (2013)

Monitoring of corrosion of pipelines of cooling system of automobile gas-filling compressor stations
von: S. A. Osadchuk, et al.
Veröffentlicht: (2011)

Procedure for Implementation of the Method of Artificial Deposition of Radioactive Substances from the Atmosphere
von: M. V. Kustov, et al.
Veröffentlicht: (2019)

List of measurement procedures for the control of atmospheric air, soil and water contamination
von: R. V. Koval, et al.
Veröffentlicht: (2016)

Improvement in cyclic life of welded T-joints under conditions of increased humidity and temperature by using high-frequency mechanical peening
von: V. V. Knysh, et al.
Veröffentlicht: (2016)

Axial coil accelerator of plasma ring in the atmospheric pressure air
von: Korytchenko, K.V., et al.
Veröffentlicht: (2019)

Accelerated testing methods for reliability prediction
von: Ja. Luste
Veröffentlicht: (2018)

Accelerated testing methods for reliability prediction
von: Ya. Luste
Veröffentlicht: (2018)

Moderate rationalism and historical studies
von: A. V. Tsarenok
Veröffentlicht: (2023)

Efficiency of strengthening by high-frequency mechanical peening of butt welded joints at long-time service
von: V. V. Knysh, et al.
Veröffentlicht: (2014)

Improvement of fatigue and corrosion resistance of welded joints by ultrasonic peening treatment and spark alloying
von: G. I. Prokopenko, et al.
Veröffentlicht: (2014)

Development of technique for testing the long-term stability of silicon microstrip detectors
von: Kosinov, A.V., et al.
Veröffentlicht: (2006)

Structural changes in metal of welded joints of steam pipelines after long term service
von: V. V. Dmytryk, et al.
Veröffentlicht: (2017)

Models of general circulation of the atmosphere and the oceans in forecasting the changes of regional climate of Ukraine in the XXI century
von: S. V. Krakovska, et al.
Veröffentlicht: (2011)

Procedure of ranging corrosion defects of the main gas pipelines found at in-pipe diagnostics
von: V. I. Makhnenko, et al.
Veröffentlicht: (2009)