Peculiarities of pore formation in welded joints of steam pipelines under conditions of long-time service

Gespeichert in:

Bibliographische Detailangaben
Datum:	2016
Hauptverfasser:	V. V. Dmitrik, A. V. Glushko, S. G. Grigorenko
Format:	Artikel
Sprache:	Englisch
Veröffentlicht:	2016
Schriftenreihe:	Automatic Welding
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0000596903
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

Features of embrittlement of welded joints of operated steam pipelines
von: V. V. Dmitrik, et al.
Veröffentlicht: (2018)

Structural changes in metal of welded joints of steam pipelines in operation
von: V. V. Dmitrik, et al.
Veröffentlicht: (2015)

Structural changes in metal of welded joints of steam pipelines after long term service
von: V. V. Dmytryk, et al.
Veröffentlicht: (2017)

Features of degradation of metal of steam pipeline welded joints
von: V. V. Dmitrik, et al.
Veröffentlicht: (2015)

Regarding mechanism of diffusion of chromium and molybdenum in metal of welded joints of steam pipelines
von: V. V. Dmitrik, et al.
Veröffentlicht: (2012)

Structural condition and damage of metal of welded joints of steam pipelines
von: V. V. Dmytryk, et al.
Veröffentlicht: (2021)

Structural condition and fatigue damageability of welded joints of steam pipelines
von: V. V. Dmytryk, et al.
Veröffentlicht: (2020)

Recovery and recrystallization of metal of steam line welded joints during long-term service
von: V. V. Dmytryk, et al.
Veröffentlicht: (2022)

Recrystallization in the metal of welding joints of steam trucks
von: Dmytryk, V.V., et al.
Veröffentlicht: (2019)

Residual stresses of circumferential welds of main gas pipeline in long-term service under the North conditions
von: N. I. Golikov, et al.
Veröffentlicht: (2012)

Efficiency of strengthening by high-frequency mechanical peening of butt welded joints at long-time service
von: V. V. Knysh, et al.
Veröffentlicht: (2014)

Evaluation of serviceability of pipeline of the first contour of WWR-M reactor with defects in welded joints
von: O. V. Makhnenko, et al.
Veröffentlicht: (2015)

Equipment for heat treatment of welded joints of pipelines
von: E. A. Pantelejmonov
Veröffentlicht: (2012)

Effect of preparation and assembly for welding on quality of welded joints of technological pipelines
von: P. V. Zankovets
Veröffentlicht: (2011)

Fatigue crack growth resistance of steels of long-term exploited steam pipeline bends
von: O. P. Ostash, et al.
Veröffentlicht: (2012)

Corrosion-resistant inhibited coatings for welded joints of pipelines
von: V. I. Pokhmurskyi, et al.
Veröffentlicht: (2013)

Restoration of heat-resistant steel properties after long-term operation in a steam pipeline
von: O. Z. Student, et al.
Veröffentlicht: (2021)

Determination of stressed state in spiral welded joint in the main pipeline
von: L. Senkiv
Veröffentlicht: (2015)

Use of mechanical resonance techniques for detection of damage in steam pipeline steels after service
von: O. V. Vdovychenko
Veröffentlicht: (2013)

Peculiarities of structure of welded joints of various-solubility metals
von: G. M. Grigorenko, et al.
Veröffentlicht: (2014)

Assessment of serviceability of long-term operating oil pipelines by the parameters of their defectiveness
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2013)

Equipment for preparation of pipe ends to welding of position butt joints of pipeline
von: L. M. Lobanov, et al.
Veröffentlicht: (2015)

Fractographic features of service degradation of welds in main oil pipelines
von: H. V. Krechkovska, et al.
Veröffentlicht: (2015)

Diagnostics of the stress-strain state of multi-layer ring welded joints of pipelines
von: Yu. V. Banakhevych, et al.
Veröffentlicht: (2014)

Tendency to crack formation in welded joints of repair structures on the gas main pipelines
von: V. S. But, et al.
Veröffentlicht: (2014)

About requirements to impact strength of pipeline joints made by flash-butt welding
von: V. I. Kirjan, et al.
Veröffentlicht: (2015)

Diagnostics of the structural-mechanical state of steam pipeline steels by coercive-metric method and prediction of their life time
von: O. P. Ostash, et al.
Veröffentlicht: (2013)

Peculiarities of formation of structure in welded joints of microalloyed structural steel S460M
von: G. M. Grigorenko, et al.
Veröffentlicht: (2017)

Peculiarities of bacterial chemotaxis in a cylindrical pore
von: O. M. Vasyliev, et al.
Veröffentlicht: (2019)

Peculiarities of bacterial chemotaxis in a cylindrical pore
von: A. N. Vasilev, et al.
Veröffentlicht: (2019)

Progress of technologies of arc welding repair of in-service main pipelines in Ukraine
von: V. S. But, et al.
Veröffentlicht: (2014)

Corrosion-mechanical resistance of 2219 alloy welded joints, under simulated service conitions
von: L. I. Nyrkova, et al.
Veröffentlicht: (2021)

Influence of 12X1M1F steel long-time operation from different zones of power station steam pipeline bend on its mechanical properties
von: O. Z. Student, et al.
Veröffentlicht: (2012)

Risk of failure during thinning of wall of main pipeline in the area of circumferential welded joints at the presence of bending moments along the axis of pipeline
von: V. I. Makhnenko, et al.
Veröffentlicht: (2012)

Stress-Strain State of Steam Turbine Lock Joint under Plastic Deformation
von: Palkov, Ihor A., et al.
Veröffentlicht: (2021)

Stress-Strain State of Steam Turbine Lock Joint under Plastic Deformation
von: Palkov, Ihor A., et al.
Veröffentlicht: (2021)

Stress-Strain State of Steam Turbine Lock Joint Under Plastic Deformation
von: I. A. Palkov, et al.
Veröffentlicht: (2020)

Determination of zones of additional control of metal and welded joints of steam generators PGV-213 at strength assessment
von: V. M. Torop, et al.
Veröffentlicht: (2013)

Methodology of multiparametral diagnostics of technical condition of pipelines in long-term operation
von: M. O. Karpash
Veröffentlicht: (2013)

Drives of mechanisms of automatic machines for orbital tig welding of metal pipeline joints in npp power units
von: N. M. Makhlin, et al.
Veröffentlicht: (2019)