Evaluation of serviceability of main pipeline with a local thinning of wall in arc surfacing repair

Gespeichert in:

Bibliographische Detailangaben
Datum:	2015
Hauptverfasser:	E. A. Velikoivanenko, G. F. Rozynka, A. S. Milenin, N. I. Pivtorak
Format:	Artikel
Sprache:	Englisch
Veröffentlicht:	2015
Schriftenreihe:	Automatic Welding
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0000467900
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

Improvement of method of assessment of risk of fracture in the zone of wall thinning in main pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2010)

Permissible pressure for filler of sealed sleeves used to repair main pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2011)

Risk of fracture of main pipeline with defects of wall thinning in repair under pressure
von: V. I. Makhnenko, et al.
Veröffentlicht: (2010)

Progress of technologies of arc welding repair of in-service main pipelines in Ukraine
von: V. S. But, et al.
Veröffentlicht: (2014)

Risk of failure during thinning of wall of main pipeline in the area of circumferential welded joints at the presence of bending moments along the axis of pipeline
von: V. I. Makhnenko, et al.
Veröffentlicht: (2012)

Peculiarities of application of split T-joints in repair and reconstruction of main pipelines under service conditions
von: V. S. But, et al.
Veröffentlicht: (2009)

Probabilistic estimate of the condition of pipeline elements with detected thinning defects
von: E. A. Velikoivanenko, et al.
Veröffentlicht: (2014)

Results of implementation of orbital welding in manufacture and repair of thin-wall pipelines
von: P. D. Zhemanjuk, et al.
Veröffentlicht: (2017)

Towards the planning of repair of main pressure pipelines on the basis of intrapipe diagnostics results
von: A. S. Milenin
Veröffentlicht: (2013)

Methodology of numerical prediction of serviceability of pipeline elements with corrosion-erosion defects under conditions of high-temperature operation
von: A. S. Milenin, et al.
Veröffentlicht: (2017)

Development of technology of mechanized arc welding in repair of main high-pressure gas pipeline
von: O. I. Olejnik, et al.
Veröffentlicht: (2016)

Behaviour of hydrogen in repair welding of pressure main pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2011)

Numerical prediction of effectiveness of reinforcement of defective pipelines by composite material bands
von: E. A. Velikoivanenko, et al.
Veröffentlicht: (2016)

Account for pore formation in estimation of limiting state in the zone of pressure vessel wall thinning defect
von: V. I. Makhnenko, et al.
Veröffentlicht: (2012)

Prediction of residual strength of pipeline elements with detected corrosion defects based on Monte-Carlo method
von: A. S. Milenin, et al.
Veröffentlicht: (2019)

Features of analysis of the technical state and support of reliability of the main gas pipelines at transportation of gashydrogen mixtures (Review)
von: O. S. Milenin, et al.
Veröffentlicht: (2022)

Numerical assessment of brittle strength of field welds of the main gas pipelines at transportation of gas-hydrogen mixtures
von: O. S. Milenin, et al.
Veröffentlicht: (2023)

Simulation of processes of initiation and propagation of subcritical damage of metal in welded pipeline elements at low-cycle loading
von: E. A. Velikoivanenko, et al.
Veröffentlicht: (2016)

Reinforcement of an NPP pipeline with a wall thinning defect by applying external weld ovelay
von: G. V. Vorona, et al.
Veröffentlicht: (2024)

Optimum reduction of operating pressure in pipeline in hardfacing repair of thinning areas
von: V. I. Makhnenko, et al.
Veröffentlicht: (2010)

Double tape for repairing local damage protective coatings of pipelines
von: L. N. Shkaraputa, et al.
Veröffentlicht: (2016)

RESEARCH INTO METHODS OF PIPE END DEMAGNETIZATION UNDER MAIN PIPELINE REPAIR
von: Dobrodeyev, P. N.
Veröffentlicht: (2014)

High-performance methods of numerical studies for solving the problems of evaluation of defective structure serviceability
von: A. S. Milenin, et al.
Veröffentlicht: (2018)

Numerical analysis of the regularities of the infuence of pipe steel degradation on the reliability of corroded main gas pipelines used for transportation of gas-hydrogen mixtures
von: O. S. Milenin, et al.
Veröffentlicht: (2024)

Biocorrosion and localization of degradation processes on main gas pipeline steel surface
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2019)

Tendency to crack formation in welded joints of repair structures on the gas main pipelines
von: V. S. But, et al.
Veröffentlicht: (2014)

Analysis of conditions of initiation and propagation of corrosion cracks in the zone of circumferential joints of main gas pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2009)

Crack initiation on pipeline inner surface in high-temperature service. Information 2. Stresses in pipe walls
von: S. A. Nedoseka, et al.
Veröffentlicht: (2015)

Evaluation of serviceability of pipeline of the first contour of WWR-M reactor with defects in welded joints
von: O. V. Makhnenko, et al.
Veröffentlicht: (2015)

Evaluation of effectiveness of repair technologies for service of power equipment
von: L. V. Kravchuk, et al.
Veröffentlicht: (2010)

Determination of contact pressure of reinforcing coupling in repair of pipelines with surface defects
von: V. I. Makhnenko, et al.
Veröffentlicht: (2013)

Method of natural gas evacuation from subject to repair area of main gas pipeline
von: T. V. Bunko, et al.
Veröffentlicht: (2018)

Electric arc welding and surfacing in repair of rails of Kiev metro
von: G. V. Kuzmenko, et al.
Veröffentlicht: (2018)

Repair of screws of extruders and automatic molding machines by plasma-arc surfacing
von: A. I. Som
Veröffentlicht: (2019)

Influence of metal shrinkage in longitudinal welds of sleeves on contact pressure in main gas pipeline repair
von: O. I. Olejnik
Veröffentlicht: (2015)

Technologies of hybrid laser-arc welding of circumferential welds on main pipelines
von: S. Kajtel, et al.
Veröffentlicht: (2014)

Development of the method for assessment of serviceability and residual life of the main pipelines with service macrodelamination
von: O. T. Tsyrulnyk, et al.
Veröffentlicht: (2020)

Diagnostics of corrosion state of internal surface of main pipeline
von: S. G. Poljakov, et al.
Veröffentlicht: (2010)

Fractographic features of service degradation of welds in main oil pipelines
von: H. V. Krechkovska, et al.
Veröffentlicht: (2015)

Numerical methodology of prediction of the reliability and residual life of welded pipeline elements with corrosion-erosion defects
von: O. S. Milenin, et al.
Veröffentlicht: (2020)