Influence of 12X1M1F steel long-time operation from different zones of power station steam pipeline bend on its mechanical properties

Gespeichert in:

Bibliographische Detailangaben
Datum:	2012
Hauptverfasser:	O. Z. Student, L. M. Svirska, I. R. Dzioba
Format:	Artikel
Sprache:	Englisch
Veröffentlicht:	2012
Schriftenreihe:	Materials Science (Physicochemical mechanics of materials)
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0000659567
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

The influence of long-term operation of 12 X1MFA steel bends of the main HPP pipelines on its mechanical properties
von: O. Z. Student, et al.
Veröffentlicht: (2017)

Fatigue crack growth resistance of steels of long-term exploited steam pipeline bends
von: O. P. Ostash, et al.
Veröffentlicht: (2012)

Restoration of heat-resistant steel properties after long-term operation in a steam pipeline
von: O. Z. Student, et al.
Veröffentlicht: (2021)

Automatic selection and quantitative analysis of carbides on the 12Kh1MF steel grains interface after operation at the HPP pipeline
von: R. A. Vorobel, et al.
Veröffentlicht: (2011)

Peculiarities of pore formation in welded joints of steam pipelines under conditions of long-time service
von: V. V. Dmitrik, et al.
Veröffentlicht: (2016)

Changing the restricded building zone in the process of the complex of basic stations for a long time
von: V. N. Evstafev, et al.
Veröffentlicht: (2017)

Anisotropy of the mechanical properties of 15Kh1M1F degraded steel after its exploitation on HPP pipelines
von: O. Z. Student, et al.
Veröffentlicht: (2011)

Structural changes in metal of welded joints of steam pipelines after long term service
von: V. V. Dmytryk, et al.
Veröffentlicht: (2017)

Assessment of steam pipeline steels degradation by impact toughness on the specimens with a cut of different-geometry
von: H. V. Krechkovska, et al.
Veröffentlicht: (2016)

Diagnostics of the technical state of steam pipelines at TPP by hardness and crack growth resistance of steel
von: H. V. Krechkovska, et al.
Veröffentlicht: (2018)

Enzymatic synthesis of 1,2-aminocyclopentanols and 1,2-diaminocyclopentanes
von: A. O. Kolodjazhna, et al.
Veröffentlicht: (2019)

Diagnostics of the structural-mechanical state of steam pipeline steels by coercive-metric method and prediction of their life time
von: O. P. Ostash, et al.
Veröffentlicht: (2013)

Meiosis course in hybrids F1—F2 T. spelta L. x T. aestivum L.
von: S. M. Sichkar, et al.
Veröffentlicht: (2017)

Inheritance of morphological characteristics in hybrids F1—F2 Triticum spelta x T. aestivum
von: S. M. Sichkar, et al.
Veröffentlicht: (2016)

Single and multi-station systems for automatic position welding of butts of nuclear power station pipelines
von: N. M. Makhlin, et al.
Veröffentlicht: (2011)

Features of embrittlement of welded joints of operated steam pipelines
von: V. V. Dmitrik, et al.
Veröffentlicht: (2018)

Features of degradation of metal of steam pipeline welded joints
von: V. V. Dmitrik, et al.
Veröffentlicht: (2015)

The influence of gas pipeline long-term operation on fatigue crack growth resistance of 17H1S steel
von: Ye. V. Kharchenko, et al.
Veröffentlicht: (2016)

Vacuum Activated Diffusion Chromium Plating of 15Kh12VNMF and 20Kh1M1F1TR Steels
von: S. G. Rudenki, et al.
Veröffentlicht: (2022)

Assessment of technological process shut-downs on the change of technical state of HPP main steam pipeline metal
von: H. M. Nykyforchyn, et al.
Veröffentlicht: (2010)

Enzymatic synthesis of enantiomerically pure 1,2-fluorocyclopentanols and 1,2-aminofluorocyclopentanes
von: O. O. Kolodiazhna, et al.
Veröffentlicht: (2019)

Enzymatic synthesis of enantiomerically pure 1,2-fluorocyclopentanols and 1,2-aminofluorocyclopentanes
von: Kolodiazhna, O.O., et al.
Veröffentlicht: (2019)

Risk of failure during thinning of wall of main pipeline in the area of circumferential welded joints at the presence of bending moments along the axis of pipeline
von: V. I. Makhnenko, et al.
Veröffentlicht: (2012)

Structural condition and damage of metal of welded joints of steam pipelines
von: V. V. Dmytryk, et al.
Veröffentlicht: (2021)

Peculiarities of damageability of welded joints of steam pipelines by creep mechanism
von: V. V. Dmitrik, et al.
Veröffentlicht: (2010)

Structural changes in metal of welded joints of steam pipelines in operation
von: V. V. Dmitrik, et al.
Veröffentlicht: (2015)

Structural condition and fatigue damageability of welded joints of steam pipelines
von: V. V. Dmytryk, et al.
Veröffentlicht: (2020)

Analysis of cytological stability interspecific hybrids F1F2 Triticum spelta x Triticum aestivum
von: I. I. Lialko, et al.
Veröffentlicht: (2016)

Qualitative Investigation of the Singular Cauchy Problem $\sum\limits_{k = 1}^n {(a_{k1} t + a_{k2} x)(x')^k = b_1 t + b_2 x + f(t,x,x'),x(0) = 0}$
von: Zernov, A. E., et al.
Veröffentlicht: (2003)

Теплоемкость возвратных ферримагнетиков Li₀,₅Fe₂,₅-xGaxO₄ с x= 0,9; 1,2
von: Ефимова, Н.Н., et al.
Veröffentlicht: (1998)

ЕЛЕКТРОПРОВІДНІСТЬ ТВЕРДИХ РОЗЧИНІВ Pb0,86‑xSmxSn1,14F4+x
von: Pohorenko, Yuliia, et al.
Veröffentlicht: (2021)

Low-cycle fatigue and cracking resistance of power plant boiler pipes and steam lines of 12Kh1MF steel
von: Zelenskii, V.G., et al.
Veröffentlicht: (1985)

Ranking of mechanical characteristics of HPP pipeline steels by their sensitivity to operational degradation
von: O. Z. Student, et al.
Veröffentlicht: (2021)

Monitoring of corrosion of pipelines of cooling system of automobile gas-filling compressor stations
von: S. A. Osadchuk, et al.
Veröffentlicht: (2011)

Organization of optimization problem of shops operating modes of gas pipelines compressor stations
von: Leshchenko
Veröffentlicht: (2006)

A Note on the Recursive Sequence $x_{n + 1} = p_kx_n + p_{k − 1}x_{n − 1} +...+ p_1x_{n − k + 1}$
von: Stevic, S., et al.
Veröffentlicht: (2003)

Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States
von: Zrilic, M., et al.
Veröffentlicht: (2004)

Regarding mechanism of diffusion of chromium and molybdenum in metal of welded joints of steam pipelines
von: V. V. Dmitrik, et al.
Veröffentlicht: (2012)

Numerical modeling transient processes in a long gas pipeline
von: V. F. Chekurin, et al.
Veröffentlicht: (2019)

Magnetic properties of multiferroics Bi1–xCaxFe1–xMnxO3 and Bi1–xCaxFe1–xTixO3
von: I. O. Trojanchuk, et al.
Veröffentlicht: (2016)