Підвищення сорбції водню допуванням мезопористого вуглецю наночастинками паладію
We have used the matrix synthesis protocol of Ryoo et al. for the preparation of highly ordered cubic mesoporous carbon (CMK-1) using mesoporous silica (MCM-48) as a template, in order to prepare palladium-doped CMK-1. The carbon obtained has a high surface area of 1800 m2g-1, a large porous volume...
Gespeichert in:
| Datum: | 2010 |
|---|---|
| Hauptverfasser: | , , , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Chuiko Institute of Surface Chemistry National Academy of Sciences of Ukraine
2010
|
| Online Zugang: | https://www.cpts.com.ua/index.php/cpts/article/view/45 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Chemistry, Physics and Technology of Surface |
Institution
Chemistry, Physics and Technology of Surface| Zusammenfassung: | We have used the matrix synthesis protocol of Ryoo et al. for the preparation of highly ordered cubic mesoporous carbon (CMK-1) using mesoporous silica (MCM-48) as a template, in order to prepare palladium-doped CMK-1. The carbon obtained has a high surface area of 1800 m2g-1, a large porous volume of 1.14 cm3g-1 and average pore diameter of 3.03 nm. Step-by-step formation of mesoporous carbon was followed by X-ray diffraction, FTIR, N2 adsorption desorption and TPD mass-spectrometry. The physical data of CMK-1 are hardly changed by Pd incorporation (CMK?1/Pd). Transmission electron microscopy and Raman spectroscopy show that the framework of the highly ordered mesoporous carbon/Pd consists of an aligned carbon phase with a graphite mode region. The potential application of CMK-1 and CMK?1/Pd as sorbents for hydrogen storage is discussed. |
|---|