ОСОБЛИВОСТІ ВПЛИВУ ДОБАВКИ VN НА СТРУКТУРУ ТА ВЛАСТИВОСТІ КОМПОЗИТУ Fe-Cu-Ni-Sn, ОТРИМАНОГО ГАРЯЧОГО ПРЕСУВАННЯ
To obtain bulk of 51Fe–32–Cu–9Ni–8Sn and 49.47Fe–31.04Cu–8.73Ni–7.76Sn–3VN nanocomposites, a pressing method at room temperature and subsequent hot pressing in a vacuum was used. The microstructure of the sintered composites by X-ray diffraction and transmission electron microscopy was investigated....
Gespeichert in:
| Datum: | 2018 |
|---|---|
| Hauptverfasser: | , , , , |
| Format: | Artikel |
| Sprache: | Russian |
| Veröffentlicht: |
Институт сверхтвердых материалов им. В. Н. Бакуля Национальной академии наук Украины
2018
|
| Schlagworte: | |
| Online Zugang: | http://altis-ism.org.ua/index.php/ALTIS/article/view/46 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Tooling materials science |
Institution
Tooling materials science| Zusammenfassung: | To obtain bulk of 51Fe–32–Cu–9Ni–8Sn and 49.47Fe–31.04Cu–8.73Ni–7.76Sn–3VN nanocomposites, a pressing method at room temperature and subsequent hot pressing in a vacuum was used. The microstructure of the sintered composites by X-ray diffraction and transmission electron microscopy was investigated. It is shown that in the 49.47Fe–31.04Cu–8.73Ni–7.76Sn–3VN composite there was a dissolution of vanadium nitride in -iron and formation of a supersaturated solid solution of nitrogen and vanadium in the г-iron. As a result, there was a substantial grinding of ferritic grains (from 5 50 μm to 20 400 nm) and improvement of mechanical characteristics occurred. Nanocomposites are considered as promising materials to create a new generation of diamond containing composites |
|---|