ФАКТОРИ ЯКОСТІ ТА НАДІЙНОСТІ ЗШИТО-ПОЛІЕТИЛЕНОВОЇ ІЗОЛЯЦІЇ СИЛОВИХ КАБЕЛІВ
The paper presents the factors and mechanisms influencing on the degradation of cross-linked polyethylene (XLPE) insulation of power cables, multiphysics processes and phenomena that take place at the aging of the insulation and lead to its breakdown. The typical defects of XLPE insulation which res...
Gespeichert in:
| Datum: | 2017 |
|---|---|
| 1. Verfasser: | |
| Format: | Artikel |
| Sprache: | Ukrainian |
| Veröffentlicht: |
Інститут електродинаміки Національної академії наук України
2017
|
| Schlagworte: | |
| Online Zugang: | https://prc.ied.org.ua/index.php/proceedings/article/view/239 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Proceedings of the Institute of Electrodynamics of the National Academy of Sciences of Ukraine |
Institution
Proceedings of the Institute of Electrodynamics of the National Academy of Sciences of Ukraine| Zusammenfassung: | The paper presents the factors and mechanisms influencing on the degradation of cross-linked polyethylene (XLPE) insulation of power cables, multiphysics processes and phenomena that take place at the aging of the insulation and lead to its breakdown. The typical defects of XLPE insulation which result from the production, design, laying and operation of the cables are shown and explained. The causes of damages and defects of the insulation are analyzed. The significance of electrical operating conditions of the cable and the need to use non-destructive testing methods for the long service life of XLPE insulation are revealed. References 49, figures 7, tables 3. |
|---|