Degradation of welded joint metal of the exploited main gas pipeline

Degradation of welded joint metal of the exploited main gas pipeline

Gespeichert in:

Bibliographische Detailangaben
Datum:	2010
Hauptverfasser:	O. T. Tsyrulnyk, V. A. Voloshyn, Yu. Petryna, M. I. Hredil, O. I. Zvirko
Format:	Artikel
Sprache:	English
Veröffentlicht:	2010
Schriftenreihe:	Materials Science (Physicochemical mechanics of materials)
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0000657369
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

Exploitation degradation of mechanical properties of ammonia pipeline metal
von: O. H. Arkhypov, et al.
Veröffentlicht: (2013)

Features of degradation of metal of steam pipeline welded joints
von: V. V. Dmitrik, et al.
Veröffentlicht: (2015)

Residual lifetime estimation for long exploited section of the main gas pipeline
von: Ye. Andreikiv, et al.
Veröffentlicht: (2012)

Corrosion degradation of long-term operated gas pipeline elbow with macrodefect
von: O. I. Zvirko, et al.
Veröffentlicht: (2016)

Tendency to crack formation in welded joints of repair structures on the gas main pipelines
von: V. S. But, et al.
Veröffentlicht: (2014)

Fractographic features of service degradation of welds in main oil pipelines
von: H. V. Krechkovska, et al.
Veröffentlicht: (2015)

Biocorrosion and localization of degradation processes on main gas pipeline steel surface
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2019)

The evaluation of operational degradation of gas pipeline steels by the mechanical stability criterion
von: Yu. Ya. Mieshkov, et al.
Veröffentlicht: (2014)

Assessment of the service degradation of a gas pipeline steel by destructive and non-destructive method
von: Yu. V. Milman, et al.
Veröffentlicht: (2011)

Influence of metal shrinkage in longitudinal welds of sleeves on contact pressure in main gas pipeline repair
von: O. I. Olejnik
Veröffentlicht: (2015)

Determination of stressed state in spiral welded joint in the main pipeline
von: L. Senkiv
Veröffentlicht: (2015)

Structural condition and damage of metal of welded joints of steam pipelines
von: V. V. Dmytryk, et al.
Veröffentlicht: (2021)

Structural changes in metal of welded joints of steam pipelines in operation
von: V. V. Dmitrik, et al.
Veröffentlicht: (2015)

Method of laboratory degradation of structural steels
von: O. T. Tsyrulnyk, et al.
Veröffentlicht: (2017)

Causes of stress corrosion fracture of site circumferential joint of main gas pipeline
von: A. A. Rybakov, et al.
Veröffentlicht: (2014)

Develop¬ment of in-laboratory method of steel degradation for assessing their crack growth resistance
von: M. I. Hredil, et al.
Veröffentlicht: (2021)

Numerical analysis of the regularities of the infuence of pipe steel degradation on the reliability of corroded main gas pipelines used for transportation of gas-hydrogen mixtures
von: O. S. Milenin, et al.
Veröffentlicht: (2024)

The influence of the operated gas pipeline steels texture on their resistance to brittle fracture
von: O. I. Zvirko, et al.
Veröffentlicht: (2018)

Development of the method for assessment of serviceability and residual life of the main pipelines with service macrodelamination
von: O. T. Tsyrulnyk, et al.
Veröffentlicht: (2020)

Calculation of residual life of main pipelines with account of environment effect and degradation of their materials
von: Ye. Andreikiv, et al.
Veröffentlicht: (2018)

The influence of the structural-mechanical state of the transit gas pipeline steel on the susceptibility to hydrogen embrittlement
von: O. I. Zvirko, et al.
Veröffentlicht: (2024)

Numerical assessment of brittle strength of field welds of the main gas pipelines at transportation of gas-hydrogen mixtures
von: O. S. Milenin, et al.
Veröffentlicht: (2023)

Analysis of conditions of initiation and propagation of corrosion cracks in the zone of circumferential joints of main gas pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2009)

Development of technology of mechanized arc welding in repair of main high-pressure gas pipeline
von: O. I. Olejnik, et al.
Veröffentlicht: (2016)

Risk of failure during thinning of wall of main pipeline in the area of circumferential welded joints at the presence of bending moments along the axis of pipeline
von: V. I. Makhnenko, et al.
Veröffentlicht: (2012)

Regarding mechanism of diffusion of chromium and molybdenum in metal of welded joints of steam pipelines
von: V. V. Dmitrik, et al.
Veröffentlicht: (2012)

Peculiarities of corrosion-hydrogen degradation of oil and gas pipelines and oil tanks
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2011)

Anisotropy of the mechanical properties of 15Kh1M1F degraded steel after its exploitation on HPP pipelines
von: O. Z. Student, et al.
Veröffentlicht: (2011)

Structural changes in metal of welded joints of steam pipelines after long term service
von: V. V. Dmytryk, et al.
Veröffentlicht: (2017)

Diagnostics of pipe steel susceptibility to property degradation as a result of long-term operation
von: H. M. Nykyforchyn, et al.
Veröffentlicht: (2016)

Analysis of causes of failure of site welded butt joints of main pipelines after long-term operation
von: L. I. Nyrkova, et al.
Veröffentlicht: (2023)

Equipment for heat treatment of welded joints of pipelines
von: E. A. Pantelejmonov
Veröffentlicht: (2012)

Corrosion-resistant inhibited coatings for welded joints of pipelines
von: V. I. Pokhmurskyi, et al.
Veröffentlicht: (2013)

Behaviour of hydrogen in repair welding of pressure main pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2011)

Influence of 17HIS steel degradation on its properties after service on the main pipeline
von: Ye. V. Kharchenko, et al.
Veröffentlicht: (2017)

Analytical methods of optimization of operational parameters of the main gas pipelines (gas mains)
von: V. Frolov, et al.
Veröffentlicht: (2018)

Effect of preparation and assembly for welding on quality of welded joints of technological pipelines
von: P. V. Zankovets
Veröffentlicht: (2011)

Features of embrittlement of welded joints of operated steam pipelines
von: V. V. Dmitrik, et al.
Veröffentlicht: (2018)

Structural condition and fatigue damageability of welded joints of steam pipelines
von: V. V. Dmytryk, et al.
Veröffentlicht: (2020)

Residual stresses of circumferential welds of main gas pipeline in long-term service under the North conditions
von: N. I. Golikov, et al.
Veröffentlicht: (2012)