Experimental and analytical evaluation of pipe steels hydrogenation

Gespeichert in:

Bibliographische Detailangaben
Datum:	2017
Hauptverfasser:	A. M. Syrotiuk, R. L. Leshchak, M. I. Dorosh
Format:	Artikel
Sprache:	Englisch
Veröffentlicht:	2017
Schriftenreihe:	Materials Science (Physicochemical mechanics of materials)
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0000823859
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

Peculiarities of deformation and fracture of low-alloyed steels in hydrogen-containing environments: influence of hydrogen concentration in metal
von: I. M. Dmytrakh, et al.
Veröffentlicht: (2018)

Effect of preliminary hydrogen charging–discharging of low-alloyed steel on its further ability to absorb electrochemical hydrogen
von: I. M. Dmytrakh, et al.
Veröffentlicht: (2021)

Features of electrochemical hydrogen charging of low-alloyed steel of pipeline in model solution of soil water
von: I. M. Dmytrakh, et al.
Veröffentlicht: (2021)

The influence of bulk hydrogen concentration in metal on peculiarities of low-alloyed pipeline steel deformation
von: I. M. Dmytrakh, et al.
Veröffentlicht: (2014)

The influence of hydrogen sulphide concentration on corrosion and hydrogenation of pipe steels (A review)
von: M. S. Khoma, et al.
Veröffentlicht: (2021)

Estimation of stresses caused by electrochemical hydrogenation of pipe carbon steel
von: O. I. Zvirko, et al.
Veröffentlicht: (2024)

The influence of texture and hydrogenation on mechanical properties and fracture behaviour of pipe steel
von: P. O. Marushchak, et al.
Veröffentlicht: (2019)

Evaluation of residual life time of hydrogenated pipe by the acoustic signal parameters
von: V. R. Skalskyi, et al.
Veröffentlicht: (2015)

Expert evaluation of technical condition of process piping with hydrogen-containing media
von: V. O. Stryzhalo, et al.
Veröffentlicht: (2015)

The influence of cyclic loading on fracture resistance of pipe steels and their weld joints in hydrogen sulphide environments
von: M. S. Khoma, et al.
Veröffentlicht: (2013)

The influence of hydrogen sulphide on carbon dioxide corrosion and mechanical characteristics of high-strength pipe steel
von: M. S. Khoma, et al.
Veröffentlicht: (2021)

Evaluation of stresses caused by the concentration of hydrogen in metals
von: M. H. Stashchuk, et al.
Veröffentlicht: (2015)

The effect of hydrogen sulfide on the corrosion and mechanical properties of pipe steel welded joints
von: H. V. Chumalo
Veröffentlicht: (2012)

Corrosion resistance of steel for boom sprayers frame
von: R. L. Leshchak, et al.
Veröffentlicht: (2020)

Evaluation of hydrogen influence on mechanical properties of 40X steel
von: Ya. L. Ivanytskyi, et al.
Veröffentlicht: (2014)

Evaluation of deformability of pipe steel joints made by automatic continuous flash-butt welding
von: S. I. Kuchuk-Jatsenko, et al.
Veröffentlicht: (2011)

The influence of welded joints defects of 17H1SU pipe steel on hydrogen sulfide stress corrosion cracking resistance
von: M. S. Khoma, et al.
Veröffentlicht: (2011)

Detection of microdefects on the surface of corroded steel pipe
von: P. O. Marushchak, et al.
Veröffentlicht: (2020)

Calculation of large polyethylene pipes with a hollow wall
von: M. H. Stashchuk, et al.
Veröffentlicht: (2012)

Calculation of the deformed state of cellular pipes in inhomogeneous soil
von: M. H. Stashchuk, et al.
Veröffentlicht: (2010)

Methods for assessing fracture and strength of pipeline steels and structures under effect of operating environments. P. II. The influence of hydrogen-containing environments
von: A. M. Syrotiuk, et al.
Veröffentlicht: (2014)

Corrosion fatigue crack growth resistance of steel for boom sprayers frame
von: A. M. Syrotiuk, et al.
Veröffentlicht: (2020)

In-service degradation of pipe steel of grounding anodes
von: O. H. Arkhypov, et al.
Veröffentlicht: (2016)

Hydrogen Brittleness and Hydrogen Plasticity of Steel
von: V. A. Soshko, et al.
Veröffentlicht: (2014)

Computer modeling of the influence of hydrogen saturation on the durability of pipe elements
von: Ming Wei, et al.
Veröffentlicht: (2021)

Numerical analysis of the regularities of the infuence of pipe steel degradation on the reliability of corroded main gas pipelines used for transportation of gas-hydrogen mixtures
von: O. S. Milenin, et al.
Veröffentlicht: (2024)

Methods of calculation of strength of polyethylene pipes with a cellular wall (A review)
von: M. H. Stashchuk, et al.
Veröffentlicht: (2013)

Kinetics of growth of corrosion cracks in pipe steel 17G1S
von: V. I. Makhnenko, et al.
Veröffentlicht: (2010)

Diagnostics of hydrogen macrodelamination in the wall of pipe elbow of a natural gas transmission pipeline
von: Ye. Kharchenko, et al.
Veröffentlicht: (2015)

Experimental and theoretical evaluation of sulfur absorption capacity of slags in production of steel with electric methods
von: D. N. Togobitskaja, et al.
Veröffentlicht: (2017)

To the choice of optimal composition of slag is desulfurization pipe steel grades
von: D. N. Togobitskaja, et al.
Veröffentlicht: (2014)

The effect of sulphides on hydrogen overtension and hydrogenation of U8 steel in chloride-hydrogen-sulphide environments
von: M. S. Khoma, et al.
Veröffentlicht: (2017)

Magnetically-impelled arc butt welding of pipes of X70 steel
von: S. I. Kuchuk-Jatsenko, et al.
Veröffentlicht: (2010)

Methodological approach and criterion of the estimation of pipe steel susceptibility to stress corrosion cracking
von: L. I. Nyrkova, et al.
Veröffentlicht: (2019)

Stress corrosion cracking of Kh70 pipe steel under cathode protection
von: L. I. Nyrkova
Veröffentlicht: (2020)

The influence of neutral soil environment on stress corrosion cracking of pipe steel
von: V. A. Voloshyn, et al.
Veröffentlicht: (2014)

Evaluation of corrosion defects in oil pipe-lines using fracture mechanics approaches
von: A. Zhiljukas, et al.
Veröffentlicht: (2010)

The influence of steels structure on corrosion, hydrogenation, stress corrosion cracking in hydrogen suplhide environments
von: M. S. Khoma, et al.
Veröffentlicht: (2019)

ropagation of a surface crack in the wall of an oil pipe, allowing for its hydrogenation
von: D. V. Rudavskyi
Veröffentlicht: (2012)

High-temperature hydrogen resistance of stainless steels
von: O. I. Balytskyi, et al.
Veröffentlicht: (2010)