Anisotropy of cyclic crack growth resistance of aluminium alloys after long-term operation

Saved in:

Bibliographic Details
Date:	2016
Main Authors:	I. M. Andreiko, Yu. V. Holovatiuk, O. P. Ostash, O. I. Semenets, L. B. Kovalchuk
Format:	Article
Language:	English
Published:	2016
Series:	Materials Science (Physicochemical mechanics of materials)
Online Access:	http://jnas.nbuv.gov.ua/article/UJRN-0000668627
Tags:	Add Tag No Tags, Be the first to tag this record!
Journal Title:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Similar Items

Low-temperature and corrosion fatigue crack growth resistance of D16ATNV and V95T1 aluminium alloys after long-term operation
by: O. P. Ostash, et al.
Published: (2014)

Low-temperature fatigue crack growth resistance of degraded B95 aluminium alloys
by: I. M. Andreiko, et al.
Published: (2012)

Evaluation of strength and crack growth resistance of railway wheels after long-term operation
by: L. I. Markashova, et al.
Published: (2011)

Diagnostics of technical condition of aircraft structures after long-term service
by: O. P. Ostash, et al.
Published: (2013)

Fatigue crack growth resistance of steels of long-term exploited steam pipeline bends
by: O. P. Ostash, et al.
Published: (2012)

Strength and cyclic crack growth resistance of thermally deformed Al–Mg–Sc alloys
by: O. P. Ostash, et al.
Published: (2021)

Influence of alloying and thermal treatment on strength and cyclic crack resistance of Al–Cu–Mg alloy welded joints. P. 2
by: T. M. Labur, et al.
Published: (2017)

Influence of alloying and thermal treatment on strength and cyclic crack resistance of Al–Cu–Mg alloy welded joints. P. 1
by: T. M. Labur, et al.
Published: (2017)

Fatigue crack growth resistance of long-term operated steel of the main oil pipeline
by: A. V. Bogdanovich, et al.
Published: (2011)

The influence of durable exploitation on the structure and physico-mechanical properties of D16 and V95 aluminium alloys
by: O. P. Ostash, et al.
Published: (2013)

Strength and fatigue crack growth resistance of as-cast graphitic steels
by: I. M. Andreiko, et al.
Published: (2013)

Creep crack growth in structuralelements under long-term loading
by: Ye. Andreikiv, et al.
Published: (2012)

Ukrainian economy: chaotic and cyclical fluctuations around the long-term growth trend
by: O. V. Pustovoit
Published: (2016)

The influence of gas pipeline long-term operation on fatigue crack growth resistance of 17H1S steel
by: Ye. V. Kharchenko, et al.
Published: (2016)

Influence of oxygenation time on crack growth in titanium alloy under cyclic bending
by: Rozumek, D., et al.
Published: (2011)

Influence of oxygenation time on crack growth in titanium alloy under cyclic bending
by: D. Rozumek, et al.
Published: (2011)

Resistance of welds of thin-sheet aluminium alloys against initiation and propagation of in-service cracks
by: A. G. Pokljatskij
Published: (2011)

Eddy current monitoring of aluminum alloy degradation during long-term operation of aircraft
by: V. M. Uchanin, et al.
Published: (2021)

Influence of irregular cyclic load on fatigue resistance of thinsheet welded joints of heat-strengthened aluminium alloys
by: V. V. Knysh, et al.
Published: (2021)

Prediction of the long-term strength heat-resistant nickel alloy
by: V. V. Krivenjuk
Published: (2009)

Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material
by: Xue, F., et al.
Published: (2015)

Cyclic cracking resistance of brittle materials in compressive loading
by: Lanin, A.G.
Published: (2009)

Strength and corrosion-fatigue crack growth resistance of Ti–Nb–Zr–Si alloys of biomedical application
by: O. P. Ostash, et al.
Published: (2019)

The influence of welds special location under welding on strength and fatigue crack growth resistance of joints
by: T. M. Labur, et al.
Published: (2016)

Long-term oxidation resistance of titanium materials for hybrid fuel cells
by: Ya. Podhurska, et al.
Published: (2021)

Experimental investigation of hot cracking susceptibility of wrought aluminium alloys
by: P. Kakh, et al.
Published: (2011)

Some features of long-term variations of galactic cosmic ray intensity and anisotropy
by: Iskra, K., et al.
Published: (2006)

Crack growth specific features under static and low-cyclic loading
by: V. A. Skachkov, et al.
Published: (2015)

Durability of Thermo-Elastohereditary Bodies under Long-Term Cyclic Loading
by: A. F. Bulat, et al.
Published: (2019)

Restoration of heat-resistant steel properties after long-term operation in a steam pipeline
by: O. Z. Student, et al.
Published: (2021)

Resistance welding of shape-memory copper—aluminium alloy
by: B. E. Paton, et al.
Published: (2015)

Selection of processing parameters for conversion coatings on high-strength aluminium alloys by cyclic voltammetry
by: L. Kwiatkowski, et al.
Published: (2014)

Selection of processing parameters for conversion coatings on high-strength aluminium alloys by cyclic voltammetry
by: Kwiatkowski, L., et al.
Published: (2014)

Labor safety during operation of machines operating at long-term cyclic loads
by: V. I. Dyrda, et al.
Published: (2019)

The influence of thermal treatment on the structure and fatigue crack growth resistance of Ti–10.3Al–3.0Zr–1.2Si alloy
by: A. D. Ivasyshyn, et al.
Published: (2014)

Formation and growth of cracks in 7075-T6 aluminium matrix hybrid FML nanocomposite materials
by: M. B. Babanli, et al.
Published: (2022)

Evaluating Approaches to Estimating Endurance and Cyclic Cracking Resistance of Metal Structure Components
by: T. I. Matchenko, et al.
Published: (2017)

Prediction of crack growth resistance of cement stone and fibre
by: V. P. Sylovaniuk, et al.
Published: (2015)

Structure and properties of aluminiums alloys after treatments by the concentrated flows of energy
by: A. D. Pogrebnjak, et al.
Published: (2007)

Present problems of vibration isolation in heavy mining machines at long-term cyclic loads
by: V. Dyrda, et al.
Published: (2020)