Fatigue crack retardation by application of repair coating on gas pipelines under pressure

Saved in:

Bibliographic Details
Date:	2012
Main Author:	T. P. Venhryniuk
Format:	Article
Language:	English
Published:	2012
Series:	Materials Science (Physicochemical mechanics of materials)
Online Access:	http://jnas.nbuv.gov.ua/article/UJRN-0000662682
Tags:	Add Tag No Tags, Be the first to tag this record!
Journal Title:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Similar Items

Tendency to crack formation in welded joints of repair structures on the gas main pipelines
by: V. S. But, et al.
Published: (2014)

Development of technology of mechanized arc welding in repair of main high-pressure gas pipeline
by: O. I. Olejnik, et al.
Published: (2016)

Behaviour of hydrogen in repair welding of pressure main pipelines
by: V. I. Makhnenko, et al.
Published: (2011)

Risk of fracture of main pipeline with defects of wall thinning in repair under pressure
by: V. I. Makhnenko, et al.
Published: (2010)

Influence of metal shrinkage in longitudinal welds of sleeves on contact pressure in main gas pipeline repair
by: O. I. Olejnik
Published: (2015)

Double tape for repairing local damage protective coatings of pipelines
by: L. N. Shkaraputa, et al.
Published: (2016)

Application of method of dry welding in repair of underwater passages of gas and oil pipelines in Russia
by: Ja. Kononenko
Published: (2010)

Optimum reduction of operating pressure in pipeline in hardfacing repair of thinning areas
by: V. I. Makhnenko, et al.
Published: (2010)

Permissible pressure for filler of sealed sleeves used to repair main pipelines
by: V. I. Makhnenko, et al.
Published: (2011)

Determination of contact pressure of reinforcing coupling in repair of pipelines with surface defects
by: V. I. Makhnenko, et al.
Published: (2013)

Peculiarities of application of split T-joints in repair and reconstruction of main pipelines under service conditions
by: V. S. But, et al.
Published: (2009)

Towards the planning of repair of main pressure pipelines on the basis of intrapipe diagnostics results
by: A. S. Milenin
Published: (2013)

The influence of gas pipeline long-term operation on fatigue crack growth resistance of 17H1S steel
by: Ye. V. Kharchenko, et al.
Published: (2016)

Method of natural gas evacuation from subject to repair area of main gas pipeline
by: T. V. Bunko, et al.
Published: (2018)

RESEARCH INTO METHODS OF PIPE END DEMAGNETIZATION UNDER MAIN PIPELINE REPAIR
by: Dobrodeyev, P. N.
Published: (2014)

Fatigue crack growth resistance of steels of long-term exploited steam pipeline bends
by: O. P. Ostash, et al.
Published: (2012)

Fatigue crack growth resistance of long-term operated steel of the main oil pipeline
by: A. V. Bogdanovich, et al.
Published: (2011)

The physiological basics of retardants application to oilseeds
by: V. H. Kuriata, et al.
Published: (2016)

Corrosion-fatigue crack growth in 20N2M steel operating pump rods
by: N. V. Kret, et al.
Published: (2020)

Modeling of multiple cracking under thermo-mechanical fatigue effect
by: H. T. Sulym, et al.
Published: (2015)

The influence of the operated gas pipeline steels texture on their resistance to brittle fracture
by: O. I. Zvirko, et al.
Published: (2018)

Fatigue life of samples after wearresistant, fabrication and repair surfacing
by: I. O. Riabtsev, et al.
Published: (2020)

Effect of car retarders on crack growth at the side frame of freight car bogie
by: V. R. Skalskyi, et al.
Published: (2021)

Effect of local temperature field on retardation of curvilinear crack with allowance of plastic deformation
by: A. B. Mustafaev
Published: (2015)

Effect of local temperature field on retardation of curvilinear crack with allowance of plastic deformation
by: Мустафаев, Азер Байрам оглы
Published: (2015)

Effect of local temperature field on retardation of curvilinear crack with allowance of plastic deformation
by: Мустафаев, Азер Байрам оглы
Published: (2015)

Electroslag technologies for repair of through-thickness cracks
by: S. M. Kozulin, et al.
Published: (2021)

Investigation of corrosion fatigue cracks of steel under wetting and drying conditions
by: Lihua Liang
Published: (2018)

Results of implementation of orbital welding in manufacture and repair of thin-wall pipelines
by: P. D. Zhemanjuk, et al.
Published: (2017)

Determination of period of subcritical creep-fatigue cracks growth under block loading
by: Ye. Andreikiv, et al.
Published: (2015)

Repair of pipelines by orbital TIG welding inside the manned space objects
by: E. G. Ternovoj, et al.
Published: (2010)

Progress of technologies of arc welding repair of in-service main pipelines in Ukraine
by: V. S. But, et al.
Published: (2014)

Creep Lifetime Assessment of Pressure-Tight PE100 Pipes Based on a Slow Fatigue Crack Growth
by: Luo, W.B., et al.
Published: (2018)

Modeling of fatigue crack growth in plates under arbitrary Mode I stress
by: Jankowiak, А., et al.
Published: (2013)

Modeling of fatigue crack growth in plates under arbitrary Mode I stress
by: A. Jankowiak, et al.
Published: (2013)

Fatigue crack growth resistance characteristics of steels under transverse shear (Review)
by: T. M. Lenkovskyi
Published: (2014)

The influence of crack faces friction on fatigue crack growth resistance of 65H steel under transverse shear
by: T. M. Lenkovskyi
Published: (2014)

Change of gas pressure, around of the main crack in uniform motion of coal backwall
by: E. P. Feldman, et al.
Published: (2017)

Pipeline pressure distribution finding methods
by: Ya. Pyanylo, et al.
Published: (2016)

Analysis of conditions of initiation and propagation of corrosion cracks in the zone of circumferential joints of main gas pipelines
by: V. I. Makhnenko, et al.
Published: (2009)